Golden Bridge ER2594 (JQ-TG2594) TIG Rod
Golden Bridge ER2594 (JQ-TG2594) TIG Rod
SKU:JQ-TG2594-1/16-0020
JQ-TG2594
JQ-TG2594 is a pure argon gas shielded TIG welding wire of austenitic-ferritic duplex stainless steel, which has excellent welding manufacturability, smooth arc, no splash and optimal bead appearance. It is permitted for all-position welding. It has good crack resistance, and is suitable for welding austenitic-ferritic duplex stainless steel.
The product is applicable for welding 022Cr25Ni10Mo3N, and is commonly used in the fields of petrochemical industry, ships and so on.
Chemical components of welding wire (%)
Item |
C |
Mn |
Si |
Cr |
Ni |
Mo |
P |
S |
Cu |
N |
| Example value | 0.021 | 2.10 | 0.56 | 25.6 | 9.75 | 3.25 | 0.011 | 0.009 | 0.15 | 0.22 |
Mechanical properties of deposited metal
Item |
Rm (MPa) |
A (%) |
| Example value | 810 | 28 |
Reference current (AC, DC-)
Diameter (mm) |
Φ1.6 |
Φ2.0 |
Φ2.5 |
Φ3.2 |
| Welding current(A) | 50-100 | 100-200 | 200-300 | 300-400 |
1. Shielding gas: Adopt pure Ar; Flow: 9-14L/min when the current is 100-200A, and 14-18L/min when the current is 200-300A.
2. Extension length of tungsten wire: 3-5mm; Arc length: 1-3mm.
3. Keep the wind speed ≤ 1.0m/s; It is suggested that argon should be introduced to the back of the welding zone for protection.
4. Pay more attention on the heat input during welding process as it will directly affect the mechanical properties and crack resistance of the weld metal.
5. The rust layer, moisture, oil stain, dust, etc. on the welding part shall be clearly removed.
The above suggestions are for reference only, and specific operation should be made according to the onsite conditions. When necessary, conduct process evaluation before determining the welding scheme.
2. Extension length of tungsten wire: 3-5mm; Arc length: 1-3mm.
3. Keep the wind speed ≤ 1.0m/s; It is suggested that argon should be introduced to the back of the welding zone for protection.
4. Pay more attention on the heat input during welding process as it will directly affect the mechanical properties and crack resistance of the weld metal.
5. The rust layer, moisture, oil stain, dust, etc. on the welding part shall be clearly removed.
The above suggestions are for reference only, and specific operation should be made according to the onsite conditions. When necessary, conduct process evaluation before determining the welding scheme.